Pitting resistance equivalent number (PREN) is a predictive measurement of a stainless steel's resistance to localized pitting corrosion based on its chemical composition. In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride .
Green death is a solution used to test the resistance of metals and alloys to corrosion. It consists of a mixture of sulfuric acid, hydrochloric acid, iron(III) chloride and copper(II) chloride and its boiling point is at approximately 103 °C. Its typical chemical composition is given in the table hereafter: [1] [2] [3] [4]
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
The salt spray test (or salt fog test) is a standardized and popular corrosion test method, used to check corrosion resistance of materials and surface coatings.Usually, the materials to be tested are metallic (although stone, ceramics, and polymers may also be tested) and finished with a surface coating which is intended to provide a degree of corrosion protection to the underlying metal.
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
Alloy 20 is an austenitic stainless steel containing less than 50% iron developed for applications involving sulfuric acid.Its corrosion resistance also finds other uses in the chemical, petrochemical, power generation, and plastics industries.
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
Tin, gold and tantalum showed high corrosion resistance similar to that of stainless steel. These materials are better though because at high temperatures the corrosion rates did not increase much. Corrosion rates at elevated temperatures increase in the presence of phosphoric acid. Sulfuric acid decreased corrosion rates.