A sieve analysis (or gradation test) is a practice or procedure used in geology, civil engineering, [1] and chemical engineering [2] to assess the particle size distribution (also called gradation) of a granular material by allowing the material to pass through a series of sieves of progressively smaller mesh size and weighing the amount of material that is stopped by each sieve as a fraction ...
Although such information contains long lists of sieve sizes, in practice sieves are normally used in series in which each member sieve is selected to pass particles approximately 1/ √ 2 smaller in diameter or 1/2 smaller in cross-sectional area than the previous sieve. For example the series 80mm, 63, 40, 31.5, 20, 16, 14, 10, 8, 6.3, 4, 2.8 ...
PSD is usually defined by the method by which it is determined. The most easily understood method of determination is sieve analysis, where powder is separated on sieves of different sizes. Thus, the PSD is defined in terms of discrete size ranges: e.g. "% of sample between 45 μm and 53 μm", when sieves of these sizes are used.
During the test, material from the test specimen that can pass through a No. 4 sieve is mixed with solutions of calcium chloride, formaldehyde and glycerin in a cylinder. The content is then left for sedimentation. After about 20 minutes, the level of clay suspension and the sand level is read on the cylinder scale.
Soil gradation is determined by analyzing the results of a sieve analysis or a hydrometer analysis. [4] [5] In a sieve analysis, a coarse-grained soil sample is shaken through a series of woven-wire square-mesh sieves. Each sieve has successively smaller openings so particles larger than the size of each sieve are retained on the sieve.
According to the Unified Soil Classification System, a #4 sieve (4 openings per inch) having 4.75 mm opening size separates sand from gravel and a #200 sieve with an 0.075 mm opening separates sand from silt and clay. According to the British standard, 0.063 mm is the boundary between sand and silt, and 2 mm is the boundary between sand and gravel.
The Fineness Modulus (FM) is an empirical figure obtained by adding the total percentage of the sample of an aggregate retained on each of a specified series of sieves, dividing the sum by 100. Sieves sizes are: 150-μm (No. 100), 300-μm (No. 50), 600-μm (No. 30), 1.18-mm (No. 16), 2.36-mm (No. 8), 4.75-mm (No. 4), 9.5-mm (3/8-in.), 19.0-mm ...
The complete test requires 500 drum revolutions at a speed of 30-33 revolutions per minute. [6] Crushed sample is then separated from fine dust on a sieve, washed, dried and weighed. [6] The test reports loss of mass to abrasion and impact, expressed as a percentage of initial sample mass. [7]