Cement hydration and strength development mainly depend on two silicate phases: tricalcium silicate (C 3 S) , and dicalcium silicate (C 2 S) . [1] Upon hydration, the main reaction products are calcium silicate hydrates (C-S-H) and calcium hydroxide Ca(OH) 2, written as CH in the cement chemist notation. C-S-H is the phase playing the role of ...
Which can also be written in the cement chemist notation as: 2C 3 S + 6H → C 3 S 2 H 3 + 3CH + 6H 2 O → C-S-H + The hydrate is referred to as the calcium silicate hydrate – "C-S-H-" – phase. It grows as a mass of interlocking needles that provide the strength of the hydrated cement system. High alite reactivity is desirable in Portland ...
Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water. This reaction typically is expressed as: 2 Ca 3 SiO 5 + 7 H 2 O → 3 CaO · 2 SiO 2 · 4 H 2 O + 3 Ca(OH) 2 + 173.6 kJ. also written in cement chemist notation, (CCN) as: 2 C 3 S + 7 H → C 3 S 2 H 4 + 3 CH + heat
Cement chemist notation (CCN) was developed to simplify the formulas cement chemists use on a daily basis. It is a shorthand way of writing the chemical formula of oxides of calcium , silicon , and various metals .
Belite is the mineral in Portland cement responsible for development of "late" strength. The other silicate, alite contributes "early" strength, due to its higher reactivity. Belite reacts with water (roughly) to form calcium silicate hydrates (C-S-H) and portlandite (Ca(OH) 2 ) according to the reaction: