The temper designation follows the cast or wrought designation number with a dash, a letter, and potentially a one to three digit number, e.g. 6061-T6. The definitions for the tempers are: [5] [6]-F : As fabricated-H : Strain hardened (cold worked) with or without thermal treatment -H1 : Strain hardened without thermal treatment
6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements.
The standard controlling its composition is maintained by The Aluminum Association. It has generally good mechanical properties and is heat treatable and weldable. It is similar to the British aluminium alloy HE9. 6063 is the most common alloy used for aluminium extrusion.
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
1060 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). It is fundamentally very similar to 1050 aluminium alloy, with the difference coming down to 0.1% aluminium by weight. However, while both 1050 and 1060 are covered by the same ISO standard, they are covered by different ASTM standards.
3003 aluminium alloy is an alloy in the wrought aluminium-manganese family (3000 or 3xxx series). It can be cold worked (but not, unlike some other types of aluminium alloys, heat-treated) to produce tempers with a higher strength but a lower ductility. Like most other aluminium-manganese alloys, 3003 is a general-purpose alloy with moderate ...
6005 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is closely related, but not identical, to 6005A aluminium alloy . The main difference between the two alloys is that 6005 has a higher minimum composition percentage of aluminium than 6005A (while having essentially the same maximum).
As a wrought alloy, it can be formed by rolling, extrusion, and forging (although forging is not common), but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility. It is generally not clad. [1] Alternate names and designations include 3.3537, N51, and A95454.