Nitriding is a heat treating process that diffuses nitrogen into the surface of a metal to create a case-hardened surface. These processes are most commonly used on low-alloy steels. These processes are most commonly used on low-alloy steels.
The process starts with a standard salt bath nitrocarburizing cycle, which produces a layer of ε iron nitride. [4] Next, the workpiece is mechanically polished; typical polishing processes include vibratory finishing, lapping, and centerless grinding. Finally, the workpiece is re-immersed into the salt quench bath for 20 to 30 minutes, rinsed ...
Their process is widely known as the Tufftride or Tenifer process. Following this, the ion nitriding process was invented in the early 1980s. This process had faster cycle times, required less cleaning and preparation, formed deeper cases, and allowed for better control of the process. [10]
During the process, atoms of carbon and nitrogen diffuse interstitially into the metal, creating barriers to slip, increasing the hardness and modulus near the surface. Carbonitriding is often applied to inexpensive, easily machined low carbon steel to impart the surface properties of more expensive and difficult to work grades of steel. [ 1 ]
Nitride forming elements must be present for this method to work; these elements include chromium, molybdenum, and aluminum. The advantage of this process is that it causes little distortion, so the part can be case-hardened after being quenched, tempered and machined. No quenching is done after nitriding.
Platinum nitride and osmium nitride may contain N 2 units, and as such should not be called nitrides. [11] [12] Nitrides of heavier members from group 11 and 12 are less stable than copper nitride (Cu 3 N) and zinc nitride (Zn 3 N 2): dry silver nitride (Ag 3 N) is a contact explosive which may detonate from the slightest touch, even a falling ...
Titanium nitride (TiN; sometimes known as tinite) is an extremely hard ceramic material, often used as a physical vapor deposition (PVD) coating on titanium alloys, steel, carbide, and aluminium components to improve the substrate's surface properties.
Aluminium nitride (Al N) is a solid nitride of aluminium. It has a high thermal conductivity of up to 321 W/(m·K) [ 5 ] and is an electrical insulator. Its wurtzite phase (w-AlN) has a band gap of ~6 eV at room temperature and has a potential application in optoelectronics operating at deep ultraviolet frequencies.