The failure of a material is usually classified into brittle failure or ductile failure . Depending on the conditions (such as temperature, state of stress, loading rate) most materials can fail in a brittle or ductile manner or both. However, for most practical situations, a material may be classified as either brittle or ductile.
The plastic deformation of ductile metals is important as it can be a sign of the potential failure of the metal. Yet, the point at which the material exhibits a ductile behavior versus a brittle behavior is not only dependent on the material itself but also on the temperature at which the stress is being applied to the material.
Ductile materials have a fracture strength lower than the ultimate tensile strength (UTS), whereas in brittle materials the fracture strength is equivalent to the UTS. [2] If a ductile material reaches its ultimate tensile strength in a load-controlled situation, [ Note 1 ] it will continue to deform, with no additional load application, until ...
Deformation mechanisms are commonly characterized as brittle, ductile, and brittle-ductile. The driving mechanism responsible is an interplay between internal (e.g. composition, grain size and lattice-preferred orientation) and external (e.g. temperature and fluid pressure) factors.
After the neck has formed in the material, further plastic deformation is concentrated in the neck while the remainder of the material undergoes elastic contraction owing to the decrease in tensile force. The stress–strain curve for a ductile material can be approximated using the Ramberg–Osgood equation. [2]
A group working under G. R. Irwin [7] at the U.S. Naval Research Laboratory (NRL) during World War II realized that plasticity must play a significant role in the fracture of ductile materials. In ductile materials (and even in materials that appear to be brittle [8]), a plastic zone develops at the tip of the crack
The brittle–ductile transition zone is characterized by a change in rock failure mode, at an approximate average depth of 10–15 km (~ 6.2–9.3 miles) in continental crust, below which rock becomes less likely to fracture and more likely to deform ductilely. The zone exists because as depth increases confining pressure increases, and ...
An object in the plastic deformation range, however, will first have undergone elastic deformation, which is undone simply be removing the applied force, so the object will return part way to its original shape. Soft thermoplastics have a rather large plastic deformation range as do ductile metals such as copper, silver, and gold.