Blast furnaces differ from bloomeries and reverberatory furnaces in that in a blast furnace, flue gas is in direct contact with the ore and iron, allowing carbon monoxide to diffuse into the ore and reduce the iron oxide. The blast furnace operates as a countercurrent exchange process whereas a bloomery does not.
The process starts by charging solid sinter and heated coke into the top of the blast furnace. Preheated air at 190 to 1,050 °C (370 to 1,920 °F) is blown into the bottom of the furnace. Zinc vapour and sulfides leave through the top and enter the condenser. Slag and lead collect at the bottom of the furnace and are tapped off regularly.
This used a blast furnace to make pig iron, which then had to undergo a further process to make forgeable bar iron. Processes for the second stage include fining in a finery forge. In the 13th century during the High Middle Ages the blast furnace was introduced by China who had been using it since as early as 200 b.c during the Qin dynasty.
The blast furnace method is expected to survive into the 22nd century because of its efficient rate of iron production at competitive costs compared with other iron-making methods. Blast furnaces keep on improving with adaptations arising from new technologies driven by rising global demand, yet the main chemical process remains the same. But ...
The coking plant that feeds a battery of blast furnaces is just as expensive as the blast furnace and requires a specific quality of coal. [ 64 ] [ 65 ] Conversely, many direct-reduction processes are disadvantaged by the costly transformation of ore into pellets: these cost on average 70% more than raw ore. [ 66 ]
The HIsarna ironmaking process is a direct reduced iron process for iron making in which iron ore is processed almost directly into liquid iron ().The process combines two process units, the Cyclone Converter Furnace (CCF) for ore melting and pre-reduction and a Smelting Reduction Vessel (SRV) where the final reduction stage to liquid iron takes place.
The blast furnace is similar in structure to a cupola furnace used in iron foundries. The furnace is charged with slag, scrap iron, limestone, coke, oxides, dross, and reverberatory slag. The coke is used to melt and reduce the lead. Limestone reacts with impurities and floats to the top. This process also keeps the lead from oxidizing. The ...
Blast furnace gas (BFG) [1] is a by-product of blast furnaces that is generated when the iron ore is reduced with coke to metallic iron. It has a very low heating value , about 3.5 MJ/m 3 (93 BTU /cu.ft), [ 2 ] because it consists of about 51 vol% nitrogen and 22 vol% carbon dioxide , which are not flammable.