In the making of firebrick, fire clay is fired in the kiln until it is partly vitrified.For special purposes, the brick may also be glazed. There are two standard sizes of fire brick: 9 in × 4 + 1 ⁄ 2 in × 3 in (229 mm × 114 mm × 76 mm) and 9 in × 4 + 1 ⁄ 2 in × 2 + 1 ⁄ 2 in (229 mm × 114 mm × 64 mm). [2]
Vermiculite is a 2:1 clay, meaning it has two tetrahedral sheets for every one octahedral sheet. It is a limited-expansion clay with a medium shrink–swell capacity . Vermiculite has a high cation-exchange capacity (CEC) at 100–150 meq /100 g.
Fire clay in a furnace. Fire clay is a range of refractory clays used in the manufacture of ceramics, especially fire brick. The United States Environmental Protection Agency defines fire clay very generally as a "mineral aggregate composed of hydrous silicates of aluminium (Al 2 O 3 ·2SiO 2 ·2H 2 O) with or without free silica." [1]
Clay engineering bricks are defined in § 6.4.51 of British Standard BS ISO 6707-1;2014 (buildings & civil engineering works - vocabulary - general terms) as "fire-clay brick that has a dense and strong semi-vitreous body and which conforms to defined limits for water absorption and compressive strength". [2]
Refractory bricks in a torpedo car used for hauling molten iron. In materials science, a refractory (or refractory material) is a material that is resistant to decomposition by heat or chemical attack and that retains its strength and rigidity at high temperatures. [1]
The compressive strength of bricks produced in the United States ranges from about 7 to 103 MPa (1,000 to 15,000 lbf/in 2), varying according to the use to which the brick are to be put. In England clay bricks can have strengths of up to 100 MPa, although a common house brick is likely to show a range of 20–40 MPa.