SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
The most common type of stainless steel, 304, has a tensile yield strength around 210 MPa (30,000 psi) in the annealed condition. It can be strengthened by cold working to a strength of 1,050 MPa (153,000 psi) in the full-hard condition.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
304 stainless steel cannot be heat treated—instead it can be strengthened by cold working. It is weakest in the annealed condition, and is strongest in the full-hard condition. The tensile yield strength ranges from 210 to 1,050 MPa (30,000 to 153,000 psi).
Type 316LN—same as 316L with nitrogen added to obtain a higher yield and tensile strength than 316L. Type 316Ti—variant of type 316 that includes titanium for heat resistance. It is used in flexible chimney liners. Type 317 [8] Type 321—similar to 304 but lower risk of weld decay due to addition of titanium.
17-4 stainless steel can be heat treated to approximately 44 Rc, [1] and an ultimate tensile strength of 1,300 MPa (190,000 psi). Its density ranges from 7,800 to 7,900 kg/m 3 (0.282 to 0.284 lb/cu in), and its modulus of elasticity ranges from 197 to 207 GPa (28.5 × 10 ^ 6 to 30.0 × 10 ^ 6 psi).