A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion, to improve the adherence of other coatings, for lubrication, or for aesthetic ...
Sulfuric acid is the most widely used solution to produce an anodized coating. Coatings of moderate thickness 1.8 μm to 25 μm (0.00007" to 0.001") [16] are known as Type II in North America, as named by MIL-A-8625, while coatings thicker than 25 μm (0.001") are known as Type III, hard-coat, hard anodizing, or engineered anodizing. Very thin ...
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
The coating is a chemical conversion of the substrate metal into its oxide, and grows both inwards and outwards from the original metal surface. Because it grows inward into the substrate, it has excellent adhesion to the substrate metal. A wide range of substrate alloys can be coated, including all wrought aluminum alloys and most cast alloys ...
Aluminium chromate conversion coatings are amorphous in structure with a gel-like composition hydrated with water. [18] Chromate conversion is a common way of passivating not only aluminium, but also zinc, cadmium, copper, silver, magnesium, and tin alloys. Anodizing is an electrolytic process that forms a thicker oxide layer.
Black oxide or blackening is a conversion coating for ferrous materials, stainless steel, copper and copper based alloys, zinc, powdered metals, and silver solder. [1] It is used to add mild corrosion resistance, for appearance, and to minimize light reflection. [ 2 ]
Bluing, being a chemical conversion coating, is not as robust against wear and corrosion resistance as plated coatings, and is typically no thicker than 2.5 micrometres (0.0001 inches). For this reason, it is considered not to add any appreciable thickness to precisely-machined parts.
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.