The twin thickness saturated once a critical residual dislocations’ density reached the coherent twin-parent crystal boundary. [ 33 ] [ 49 ] Significant attention has been paid to the crystallography , [ 50 ] morphology [ 51 ] and macro mechanical effects [ 52 ] of deformation twinning.
A twin boundary is a defect that introduces a plane of mirror symmetry in the ordering of a crystal. For example, in cubic close-packed crystals, the stacking sequence of a twin boundary would be ABCABCBACBA. On planes of single crystals, steps between atomically flat terraces can also be regarded as planar defects.
In materials science, a grain boundary is the interface between two grains, or crystallites, in a polycrystalline material. Grain boundaries are two-dimensional defects in the crystal structure , and tend to decrease the electrical and thermal conductivity of the material.
Depending upon the relative energies of {111} and {110} facets, the shape can range from an icosahedron (on the left of the figure) with small dents at the five-fold axes (due to the twin boundary energy) when {111} is significantly lower in energy, to (going to the right in the figure) a truncated icosahedron or a Icosidodecahedron when the ...
On either side of this domain, the lattice is still perfect, and the boundaries of the domain are referred to as antiphase boundaries. [1] Crucially, crystals on either side of an antiphase boundary are related by a translation, rather than a reflection (a crystal twin) or an inversion (an inversion domain).
Twinning is a phenomenon somewhere between a crystallographic defect and a grain boundary. Like a grain boundary, a twin boundary has different crystal orientations on its two sides. But unlike a grain boundary, the orientations are not random, but related in a specific, mirror-image way. Mosaicity is a spread of crystal plane orientations.
Among the grain boundaries, it is known that the twin boundaries, a special type of low-energy grain boundary has lower interaction energy with dislocation leading to much smaller saturation size of the grain. [13] The cryogenic dynamic plastic deformation creates higher fraction of the twin boundaries compared to the severe plastic deformation.