The plastic section modulus is calculated as the sum of the areas of the cross section on either side of the PNA, each multiplied by the distance from their respective local centroids to the PNA. [16] = + where: A C is the area in compression A T is the area in tension y C, y T are the distances from the PNA to their centroids. Plastic section ...
ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3). ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M.
ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada.
The farther a given amount of material is from the neutral axis, the larger is the section modulus and hence a larger bending moment can be resisted. When designing a symmetric I-beam to resist stresses due to bending the usual starting point is the required section modulus. If the allowable stress is σ max and the maximum expected bending ...
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
Steel never turns into a liquid below this temperature. Pure Iron ('Steel' with 0% Carbon) starts to melt at 1,492 °C (2,718 °F), and is completely liquid upon reaching 1,539 °C (2,802 °F). Steel with 2.1% Carbon by weight begins melting at 1,130 °C (2,070 °F), and is completely molten upon reaching 1,315 °C (2,399 °F).
Elastic properties describe the reversible deformation (elastic response) of a material to an applied stress.They are a subset of the material properties that provide a quantitative description of the characteristics of a material, like its strength.
English: The cross-section of an I-beam with dimensions for calculating the section modulus. The arrow indicates that the section modulus is being calculated for the weak axis. The arrow indicates that the section modulus is being calculated for the weak axis.