The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F), depending on the alloy in question. This process is mainly suited for low-carbon steel. The material is heated up to a temperature just below the lower critical temperature of steel.
The recrystallization temperature is temperature at which recrystallization can occur for a given material and processing conditions. This is not a set temperature and is dependent upon factors including the following: [3] Increasing annealing time decreases recrystallization temperature
The steel is usually heated to 550 to 650 °C (1,000 to 1,200 °F) for 1 hour, but sometimes temperatures as high as 700 °C (1,300 °F). The image above shows the process annealing area. Isothermal annealing It is a process in which hypoeutectoid steel is heated above the upper critical temperature.
Normalizing not only produces pearlite but also martensite and sometimes bainite, which gives harder and stronger steel but with less ductility for the same composition than full annealing. In the normalizing process the steel is heated to about 40 degrees Celsius above its upper critical temperature limit, held at this temperature for some ...
From the steel boundary these are named the Gamma (Γ), Zeta (ζ), and Delta (δ) layers, of compositions Fe 3 Zn 10, FeZn 10, FeZn 13 respectively; resulting in an overall bulk iron content of 9-12%. The layers also contain around 1-4% aluminium. Composition depends primarily on heating time and temperature, limited by the diffusion of the two ...
Differentially tempered steel. The various colors produced indicate the temperature the steel was heated to. Light straw indicates 204 °C (399 °F) and light blue indicates 337 °C (639 °F). [1] [2] Tempering is a process of heat treating, which is used to increase the toughness of iron-based alloys.