Insulating glass units (IGUs) are typically manufactured with glass in thicknesses from 3 to 10 mm (1/8" to 3/8"). Thicker glass is used in special applications. Laminated or tempered glass may also be used as part of the construction.
Bulletproof glass varies in thickness from 3 ⁄ 4 to 3 + 1 ⁄ 2 inches (19 to 89 mm). [ 2 ] [ 3 ] Bulletproof glass is used in windows of buildings that require such security, such as jewelry stores and embassies, and of military and private vehicles.
In automobiles, the laminated glass panel is around 6.5 mm (0.26 inches) thick, in comparison to airplane glass being three times as thick. [21] In airliners on the front and side cockpit windows, there is often three plies of 4 mm toughened glass with 2.6 mm thick PVB between them.
The film thickness is selected for level of protection desired and the dimensions of the glass pane. Manufacturers recommend 100 micrometer film (2 ply) for glass up to 3 mm (1/8 in) and 175 micrometer film for glass over 6 mm (1/4 in). These films can be applied for security applications, where a delay of forced entry is desired.
[1] [2] The more rapid contraction of the outer layer during manufacturing induces compressive stresses in the surface of the glass balanced by tensile stresses in the body of the glass. Fully tempered 6-mm thick glass must have either a minimum surface compression of 69 MPa (10 000 psi) or an edge compression of not less than 67 MPa (9 700 psi ...
Glass thicknesses typically range from 2.0 to 2.5 millimetres (0.079 to 0.098 in). Clear glass has light transmission of approximately 90%, absorption of approximately 2%, and reflection of approximately 8%. Whereas absorption can be reduced by using low-iron glass, reflection can only be reduced by an anti-reflective surface treatment.
The ideal gap size varies by location, but on average it ranges from 15-18 mm thick, giving a final assembly size of 23-26 mm assuming a typical glazing thickness of 4 mm. [9] A double-paned window with air in the gap has an R-value of 2.1, which is much better than the 0.9 that a single pane of glass yields. A triple-paned window, which is not ...
Soda–lime glass (for containers) [2] Borosilicate (low expansion, similar to Pyrex, Duran) Glass wool (for thermal insulation) Special optical glass (similar to Lead crystal) Fused silica Germania glass Germanium selenide glass Chemical composition, wt% 74 SiO 2, 13 Na 2 O, 10.5 CaO, 1.3 Al 2 O 3, 0.3 K 2 O, 0.2 SO 3, 0.2 MgO, 0.01 TiO 2, 0. ...