AISI grade [7] C Cr Mo Ni Others Melts at [8] Remark 1.4310 X10CrNi18-8 301 0.10 17.5 NS: 8 NS: 1420 For springs 1.4301 X5CrNi18-10 304 < 0.07 18.5 NS: 9 NS: 1450 A very common austenitic stainless steel grade 1.4307 X2CrNi18-9 304L < 0.030 18.5 NS: 9 NS: 1450 Similar to the above but not susceptible to intergranular corrosion thanks to a lower ...
The weldability, also known as joinability, [1] of a material refers to its ability to be welded. Many metals and thermoplastics can be welded, but some are easier to weld than others (see Rheological weldability). A material's weldability is used to determine the welding process and to compare the final weld quality to other materials.
The carbon content of 304L (UNS 30403) is restricted to a maximum of 0.035%, which prevents sensitization during welding. Sensitization is the formation of chromium carbides along grain boundaries when stainless steel is exposed to temperatures in the approximate range of 480–820 °C (900–1,500 °F).
The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International.. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels.
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
Inconel 925: Inconel 925 is a nonstabilized austenitic stainless steel with low carbon content. [74] Inconel 939: Gamma prime strengthened to increase weldability; In age hardening or precipitation strengthening varieties, alloying additions of aluminum and titanium combine with nickel to form the intermetallic compound Ni 3 (Ti,Al) or gamma ...
The carbon equivalent is a measure of the tendency of the weld to form martensite on cooling and to suffer brittle fracture. When the carbon equivalent is between 0.40 and 0.60 weld preheat may be necessary. When the carbon equivalent is above 0.60, preheat is necessary, postheat may be necessary.
SAE 310 stainless steel is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the steel excellent oxidation resistance as well as high strength at high temperature.