Heat treatment involves the use of heating or chilling, normally to extreme temperatures, to achieve the desired result such as hardening or softening of a material. Heat treatment techniques include annealing, case hardening, precipitation strengthening, tempering, carburizing, normalizing and quenching.
The high temperature of annealing may result in oxidation of the metal's surface, resulting in scale. If scale must be avoided, annealing is carried out in a special atmosphere, such as with endothermic gas (a mixture of carbon monoxide, hydrogen gas, and nitrogen gas). Annealing is also done in forming gas, a mixture of hydrogen and nitrogen.
Tempering is a process of heat treating, which is used to increase the toughness of iron-based alloys. Tempering is usually performed after hardening, to reduce some of the excess hardness, and is done by heating the metal to some temperature below the critical point for a certain period of time, then allowing it to cool in still air. The exact ...
The term hardened steel is often used for a medium or high carbon steel that has been given heat treatment and then quenching followed by tempering. The quenching results in the formation of metastable martensite, the fraction of which is reduced to the desired amount during tempering. This is the most common state for finished articles such as ...
As with conventional quench and tempering the material being heat treated must be cooled from the austenitizing temperature quickly enough to avoid the formation of pearlite. The specific cooling rate that is necessary to avoid the formation of pearlite is a product of the chemistry of the austenite phase and thus the alloy being processed.
Equipment. Consolidated Engineering Company Archived 2013-11-05 at the Wayback Machine Annealing furnaces cover a broad range of Steel and Aluminum applications including tempering, normalizing, and aging, and similar automated loading, unloading and natural or forced cooling is possible with roller hearth, tip-up or batch arrangements.
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
In the martempering process, austenitized metal part is immersed in a bath at a temperature just above the martensite start temperature (Ms). By using interrupted quenching, the cooling is stopped at a point above the martensite transformation region to ensure sufficient time for the center to cool to the same temperature as the surface.