The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
17-4 stainless steel can be heat treated to approximately 44 Rc, [1] and an ultimate tensile strength of 1,300 MPa (190,000 psi). Its density ranges from 7,800 to 7,900 kg/m 3 (0.282 to 0.284 lb/cu in), and its modulus of elasticity ranges from 197 to 207 GPa (28.5 × 10 ^ 6 to 30.0 × 10 ^ 6 psi).
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [ 7 ] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa ) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
The "HY" steels are designed to possess a high yield strength (strength in resisting permanent plastic deformation). HY-80 is accompanied by HY-100 and HY-130 with each of the 80, 100 and 130 referring to their yield strength in ksi (80,000 psi, 100,000 psi and 130,000 psi). HY-80 and HY-100 are both weldable grades, whereas the HY-130 is ...
A514 is a particular type of high strength steel, which is quenched and tempered alloy steel, with a yield strength of 100,000 psi (100 ksi or approximately 700 MPa). The ArcelorMittal trademarked name is T-1. [1] A514 is primarily used as a structural steel for building construction.
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.
The yield strength or yield stress is a material property and is the stress corresponding to the yield point at which the material begins to deform plastically. The yield strength is often used to determine the maximum allowable load in a mechanical component, since it represents the upper limit to forces that can be applied without producing ...
Print/export Download as PDF ... 4340 steel is an ultra-high strength ... The mechanical properties of 4340 are highly dependent on the heat treatment. 4340 can ...