The solubility of magnesium is very high in aluminium and reaches a maximum at 450 °C with 14% to 17% depending on the literature reference. At 34.5%, there is a Eutectic with Al 8 Mg 5 (sometimes referred to as Al 3 Mg 2), an intermetallic phase (-phase).
Marking AZ91A for example conveys magnesium alloy with roughly 9 weight percent aluminium (between 8.6 and 9.4) and 1 weight percent zinc (between 0.6 and 1.4), and the final A means it was the first alloy with this composition at the time of registration. Exact composition should be confirmed from reference standards.
5052 is an aluminium–magnesium alloy, primarily alloyed with magnesium and chromium. 5052 is not a heat treatable aluminum ... Magnesium - 2.2%-2.8% by weight;
An aluminium alloy (UK/IUPAC) or aluminum alloy (NA; see spelling differences) is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper , magnesium , manganese , silicon , tin , nickel and zinc .
6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements.
An average 70 kg human body is about 0.01% heavy metals (~7 g, equivalent to the weight of two dried peas, with iron at 4 g, zinc at 2.5 g, and lead at 0.12 g comprising the three main constituents), 2% light metals (~1.4 kg, the weight of a bottle of wine) and nearly 98% nonmetals (mostly water).
The content of magnesium is greater than that of silicon, otherwise they belong to the aluminum–silicon–magnesium alloys (AlSiMg). AlMgSi is one of the hardenable aluminum alloys, i.e. those that can become firmer and harder through heat treatment. This curing is largely based on the excretion of magnesium silicide (Mg 2 Si). The AlMgSi ...
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.