The Los Angeles abrasion test (LA abrasion) is the North American standard for testing toughness (resistance to abrasion and degradation [1]) of construction aggregate or gravel and its suitability for road construction. Test methodology and equipment is defined in the ASTM International publications ASTM C131 for particle sizes smaller than 37 ...
A first-order estimate of the relation between ASTM D2240 type D hardness (for a conical indenter with a 15° half-cone angle) and the elastic modulus of the material being tested is [10] = (+ +), where is the ASTM D2240 type D hardness, and is in MPa.
The governing standard for the Barcol hardness test is ASTM D 2583. [4] Barcol hardness is measured on a scale from 0 to 100 with the typical range being between 50B and 90B. A measurement of 60B is roughly equivalent to a Shore hardness of 80D or a Rockwell hardness M100.
ASTM International, formerly known as American Society for Testing and Materials, is a standards organization that develops and publishes voluntary consensus technical international standards for a wide range of materials, products, systems and services. Some 12,575 apply globally.
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
ASTM G99 Standard Test Method for Wear Testing with a Pin-on-Disk Apparatus [20] ASTM G105 Standard Test Method for Conducting Wet Sand/Rubber Wheel Abrasion Tests [21] ASTM G132 Standard Test Method for Pin Abrasion Testing [22] ASTM G171 Standard Test Method for Scratch Hardness of Materials Using a Diamond Stylus [23] ASTM G174 Standard Test ...
A test takes a mere 2 seconds and, using the standard probe D, leaves an indentation of just ~0.5 mm in diameter on steel or steel casting with a Leeb hardness of 600 HLD. By comparison, a Brinell indentation on the same material is ~3 mm (hardness value ~400 HBW 10/3000), with a standard-compliant measuring time of ~15 seconds plus the time ...
Abrasion resistant steel undergoes a two-step heat treatment process called quenching and tempering, which alters the steel's grain structure to increase hardness and toughness. [2] During the quenching phase, the steel is heated to an above-critical temperature and is then rapidly cooled with water.