The NaOH (caustic soda) and elevated temperature cause Fe 3 O 4 (black oxide) to form on the surface of the metal instead of Fe 2 O 3 (red oxide; rust). While it is physically denser than red oxide, the fresh black oxide is porous, so oil is then applied as post treatment to the heated part, which seals it by "sinking" into it.
This is an alternative method for creating the black oxide coating. In place of using a hot bath (although at a lower temperature) chemically induced method, it is possible through controlling the temperature to heat steel precisely such as to cause the formation of black oxide selectively over the red oxide.
Tannic acid chemically converts the reddish iron oxides into bluish-black ferric tannate, a more stable material. [2] The second active ingredient is an organic solvent such as 2-butoxyethanol (ethylene glycol monobutyl ether, trade name butyl cellosolve) that acts as a wetting agent and provides a protective primer layer in conjunction with an ...
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion , to improve the adherence of other coatings, for lubrication , or for aesthetic ...
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting.
An additional step can be added to the nitrocarburizing process called post-oxidation. When properly performed, post-oxidation creates a layer of black oxide (Fe 3 O 4), that greatly increases the corrosion resistance of the treated substrate while leaving an aesthetically attractive black color. [28]