Calcium aluminates phase diagram Crystal structure of dodecacalcium hepta-aluminate, 12CaO·7Al 2 O 3 (C 12 A 7). [1] Calcium aluminates are a range of materials [2] obtained by heating calcium oxide and aluminium oxide together at high temperatures. They are encountered in the manufacture of refractories and cements.
Monocalcium aluminate is formed when the appropriate proportions of calcium carbonate and aluminium oxide are heated together until the mixture melts. It melts incongruently at 1390 °C. The crystal is monoclinic and pseudohexagonal , and has density 2945 kg·m −3 .
The following chart shows the solubility of various ionic compounds in water at 1 atm pressure and room temperature (approx. 25 °C, 298.15 K). "Soluble" means the ionic compound doesn't precipitate, while "slightly soluble" and "insoluble" mean that a solid will precipitate; "slightly soluble" compounds like calcium sulfate may require heat to precipitate.
Tricalcium aluminate Ca 3 Al 2 O 6, often formulated as 3CaO·Al 2 O 3 to highlight the proportions of the oxides from which it is made, is the most basic of the calcium aluminates. It does not occur in nature, but is an important mineral phase in Portland cement .
Calcium aluminates can form complex salts in combination with different types of anions.Two series of calcium aluminates are known in cement chemistry: AFm and AFt phases, being respectively mono- or tri-substituted with a given divalent anion X (e.g. SO 2− 4, CO 2− 3, or hosting a divalent impurity such as SeO 2− 4 [3]...), or with two units of a monovalent anion, e.g. OH −, Cl − ...
Dodecacalcium hepta-aluminate (12CaO·7Al 2 O 3, Ca 12 Al 14 O 33 or C 12 A 7) is an inorganic solid that occurs rarely in nature as the mineral mayenite. It is an important phase in calcium aluminate cements and is an intermediate in the manufacture of Portland cement. Its composition and properties have been the subject of much debate ...
Calcium aluminoferrite (Ca 2 (Al,Fe) 2 O 5) is a dark brown crystalline phase commonly found in cements. In the cement industry it is termed tetra-calcium aluminoferrite or ferrite. In cement chemist notation (CCN), it is abbreviated as C 4 AF meaning 4CaO· Al 2 O 3 · Fe 2 O 3 in the oxide notation. It also exists in nature as the rare ...
The aluminium, iron, and magnesium oxides are present as a flux allowing the calcium silicates to form at a lower temperature, [15] and contribute little to the strength. For special cements, such as low heat (LH) and sulphate resistant (SR) types, it is necessary to limit the amount of tricalcium aluminate (3 CaO·Al 2 O 3) formed.