Semi-crystalline polymers with strong crystalline regions resist deformation and cavitation, the formation of voids in the amorphous phase, drives yielding. [25] As done in crystalline materials, particles can be added to semi-crystalline polymers to change the mechanical properties.
Many plastics are completely amorphous (without a highly ordered molecular structure), [22] including thermosets, polystyrene, and methyl methacrylate (PMMA). Crystalline plastics exhibit a pattern of more regularly spaced atoms, such as high-density polyethylene (HDPE), polybutylene terephthalate (PBT), and polyether ether ketone (PEEK ...
All polymers (amorphous or semi-crystalline) go through glass transitions. The glass-transition temperature ( T g ) is a crucial physical parameter for polymer manufacturing, processing, and use. Below T g , molecular motions are frozen and polymers are brittle and glassy.
Depending on its processing and thermal history, polyethylene terephthalate may exist both as an amorphous (transparent) and as a semi-crystalline polymer. The semicrystalline material might appear transparent (particle size less than 500 nm ) or opaque and white (particle size up to a few micrometers ) depending on its crystal structure and ...
In condensed matter physics and materials science, an amorphous solid (or non-crystalline solid) is a solid that lacks the long-range order that is a characteristic of a crystal. The terms " glass " and "glassy solid" are sometimes used synonymously with amorphous solid; however, these terms refer specifically to amorphous materials that ...
This has an impact on the crystallinity (amorphous or semi-crystalline) and the thermal properties (expressed as glass transition point T g and melting point T m). The term tacticity describes for polypropylene how the methyl group is oriented in the polymer chain. Commercial polypropylene is usually isotactic.
In the case of polymers, conformational changes of segments, typically consisting of 10–20 main-chain atoms, become infinitely slow below the glass transition temperature. In a partially crystalline polymer the glass transition occurs only in the amorphous parts of the material. The definition is different from that in ref. [9]
Amorphous and semi-amorphous plastics are less resistant to chemical attack and environmental stress cracking because they lack a crystalline structure. Brittleness can be decreased with the addition of plasticizers , which increases the mobility of amorphous chain segments to effectively lower the glass transition temperature.