A useful tool for dealing with high frequency magnetic effects is the complex permeability. While at low frequencies in a linear material the magnetic field and the auxiliary magnetic field are simply proportional to each other through some scalar permeability, at high frequencies these quantities will react to each other with some lag time. [36]
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
Magnetic field (green) created by a current-carrying winding (red) in a typical magnetic core transformer or inductor, with the iron core C forming a closed loop, possibly with air gaps G in it. The drawing shows a section through the core. The purpose of the core is to provide a closed high permeability path for the magnetic field lines.
By choosing a magnetic material with a high (BH) max, and also choosing the aspect ratio of the magnet so that its −BH is equal to (BH) max, the required volume of magnet to achieve a target flux density in the air gap is minimized. This expression assumes that the permeability in the core that is connecting the magnetic material to the air ...
The high permeability of mu-metal provides a low reluctance path for magnetic flux, leading to its use in magnetic shields against static or slowly varying magnetic fields. Magnetic shielding made with high-permeability alloys like mu-metal works not by blocking magnetic fields but by providing a path for the magnetic field lines around the ...
In other words, the easy axis is an energetically favorable direction of spontaneous magnetization. Because the two opposite directions along an easy axis are usually equivalently easy to magnetize along, the actual direction of magnetization can just as easily settle into either direction, which is an example of spontaneous symmetry breaking.
The permeability of ferromagnetic materials is not constant, but depends on H. In saturable materials the relative permeability increases with H to a maximum, then as it approaches saturation inverts and decreases toward one. [2] [3] Different materials have different saturation levels.
Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000) [ clarification needed ] , low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T [ clarification needed ] .